KAVAN Epoxy putty 56g

Product detailed description

Quick-hardening, hand-mixable, two-component epoxy putty, malleable and moldable like plasticine. After complete hardening, it is waterproof and easy to process by hand or by machine - it is easy to grind, drill, etc. Excellent resistance to fuels, solvents and many chemicals. The hardened product can be painted with all kinds of colors. For sealing and repairing cracks, fissures, holes; repairs of damaged edges, sealing of porous surfaces. Excellent for sealing water pools (hardens even under water), as a modeling putty that adheres well to wood, metals, glass, ceramics, masonry and many plastics. You can use it to create small parts and model details - by pressing into a suitable mold or by rough shaping and subsequent processing of the hardened material.

Features

• Mixing ratio of components: 1:1 (by volume and weight)
• Initial color: green/white
• Final color: green
• Working time (plastic/moldable): 2–2.5 min
• Working time (until solidification): approx. 5 min (at 23 °C)
• Processing temperature: >15 °C
• The plastered objects can be handled: after 15–25 min
• Full strength: 35–45 min
• Full curing: 24 h
• Temperature resistance of hardened sealant: up to +120 °C, short-term up to +150 °C
• Removing excess uncured sealant: a cloth or paper napkin moistened with denatured alcohol.

Suitable for sealing: soft and hard wood, chipboard, plywood, metals, compact polystyrene, non-softened PVC, PSH and ABS, ceramics, porcelain, glass and carbon laminates.

Not suitable for sealing: soft and flexible plastics (including EPP and EPO), polyethylene, polypropylene, Teflon.

Storage: in a cool (10 °C to 25 °C), dry and dark place. Do not expose to temperatures below 10 °C. Be careful not to mix the sealant components when separating the required amount of material - even a small amount of hardener can spoil a large amount of resin.

Durability: if the conditions of proper storage are observed, we guarantee the durability of the unopened product for a period of 1 year while maintaining the above-mentioned properties.